Title: Effects of direct fluorination on space charge accumulation in HTV silicone rubber
Authors: B. X. Du;Z. L. Li;Jin Li
subject: trap level|isothermal discharge current|direct fluorination|HVDC cable|space charge|HTV Silicone Rubber|cable accessories
Year: 2016
Publisher: IEEE
Abstract: HTV silicone rubber (SiR), due to its better electrical insulation, elasticity, temperature resistance, is used in cable accessories for HVDC cables. The space charge, formed under dc stress in SiR, would distort the local electric field, and furtherly influence the characteristics of partial discharge and accelerate the insulation aging. Direct fluorination, as a solution to change the chemical component, could alter the electrical properties of the polymer surface layer. This paper focuses on the effect of the fluorination on the space charge accumulation in HTV SiR. In this investigation, the samples were fluorinated at 25 ° using a F2/N2 mixture gas with 20 % F2 by volume at 0.05 MPa for 10, 20, 30 and 40 minutes. The space charge behavior of the fluorinated samples was observed by PEA method and the trap level distribution was obtained by modified isothermal discharge current (MIDC) test. The results indicated that the fluorination for 20 minutes effectively suppressed the space charge injection in SiR. However, excessive fluorination (over 30 minutes) brought in abundant deep traps, and led to significant amount of space charge accumulation in the bulk of polymer. As a consequence, the appropriate fluorination has significant effect on the space charge accumulation in HTV SiR and has a potential application for inner insulation in premolded accessories of HVDC cable.
Description: 
URI: http://localhost/handle/Hannan/170270
http://localhost/handle/Hannan/658650
ISSN: 1070-9878
volume: 23
issue: 4
Appears in Collections:2016

Files in This Item:
File Description SizeFormat 
7556513.pdf2.21 MBAdobe PDFThumbnail
Preview File
Title: Effects of direct fluorination on space charge accumulation in HTV silicone rubber
Authors: B. X. Du;Z. L. Li;Jin Li
subject: trap level|isothermal discharge current|direct fluorination|HVDC cable|space charge|HTV Silicone Rubber|cable accessories
Year: 2016
Publisher: IEEE
Abstract: HTV silicone rubber (SiR), due to its better electrical insulation, elasticity, temperature resistance, is used in cable accessories for HVDC cables. The space charge, formed under dc stress in SiR, would distort the local electric field, and furtherly influence the characteristics of partial discharge and accelerate the insulation aging. Direct fluorination, as a solution to change the chemical component, could alter the electrical properties of the polymer surface layer. This paper focuses on the effect of the fluorination on the space charge accumulation in HTV SiR. In this investigation, the samples were fluorinated at 25 ° using a F2/N2 mixture gas with 20 % F2 by volume at 0.05 MPa for 10, 20, 30 and 40 minutes. The space charge behavior of the fluorinated samples was observed by PEA method and the trap level distribution was obtained by modified isothermal discharge current (MIDC) test. The results indicated that the fluorination for 20 minutes effectively suppressed the space charge injection in SiR. However, excessive fluorination (over 30 minutes) brought in abundant deep traps, and led to significant amount of space charge accumulation in the bulk of polymer. As a consequence, the appropriate fluorination has significant effect on the space charge accumulation in HTV SiR and has a potential application for inner insulation in premolded accessories of HVDC cable.
Description: 
URI: http://localhost/handle/Hannan/170270
http://localhost/handle/Hannan/658650
ISSN: 1070-9878
volume: 23
issue: 4
Appears in Collections:2016

Files in This Item:
File Description SizeFormat 
7556513.pdf2.21 MBAdobe PDFThumbnail
Preview File
Title: Effects of direct fluorination on space charge accumulation in HTV silicone rubber
Authors: B. X. Du;Z. L. Li;Jin Li
subject: trap level|isothermal discharge current|direct fluorination|HVDC cable|space charge|HTV Silicone Rubber|cable accessories
Year: 2016
Publisher: IEEE
Abstract: HTV silicone rubber (SiR), due to its better electrical insulation, elasticity, temperature resistance, is used in cable accessories for HVDC cables. The space charge, formed under dc stress in SiR, would distort the local electric field, and furtherly influence the characteristics of partial discharge and accelerate the insulation aging. Direct fluorination, as a solution to change the chemical component, could alter the electrical properties of the polymer surface layer. This paper focuses on the effect of the fluorination on the space charge accumulation in HTV SiR. In this investigation, the samples were fluorinated at 25 ° using a F2/N2 mixture gas with 20 % F2 by volume at 0.05 MPa for 10, 20, 30 and 40 minutes. The space charge behavior of the fluorinated samples was observed by PEA method and the trap level distribution was obtained by modified isothermal discharge current (MIDC) test. The results indicated that the fluorination for 20 minutes effectively suppressed the space charge injection in SiR. However, excessive fluorination (over 30 minutes) brought in abundant deep traps, and led to significant amount of space charge accumulation in the bulk of polymer. As a consequence, the appropriate fluorination has significant effect on the space charge accumulation in HTV SiR and has a potential application for inner insulation in premolded accessories of HVDC cable.
Description: 
URI: http://localhost/handle/Hannan/170270
http://localhost/handle/Hannan/658650
ISSN: 1070-9878
volume: 23
issue: 4
Appears in Collections:2016

Files in This Item:
File Description SizeFormat 
7556513.pdf2.21 MBAdobe PDFThumbnail
Preview File